HF 5670

Posted Leave a commentPosted in high flow grades

PROPERTIES Test- Method ASTM Test condition Unit HF- 5670 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 670(9,530) Elongation at break D-638 5mm/min % 3.5 Flexural strength D-790 2.8mm/min kg/cm2(psi) 700(9,960) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 35,900(510) IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.3(0.42) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]

HF 5661HC

Posted Leave a commentPosted in high flow grades

PROPERTIES Test- Method ASTM Test condition Unit HF- 5661HC Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 770(10,950) Elongation at break D-638 5mm/min % 5.2 Flexural strength D-790 2.8mm/min kg/cm2(psi) 1,190(16,900) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 31,000(449) IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.7(0.5) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]

HF 5661H

Posted Leave a commentPosted in high flow grades

PROPERTIES Test- Method ASTM Test condition Unit HF- 5661H Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 740(10,530) Elongation at break D-638 5mm/min % 4.6 Flexural strength D-790 2.8mm/min kg/cm2(psi) 1,170(16,640) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 31,500 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.4(0.44) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]

HF 5661

Posted Leave a commentPosted in high flow grades

PROPERTIES Test- Method ASTM Test condition Unit HF- 5661 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 690(9,810) Elongation at break D-638 5mm/min % 4.2 Flexural strength D-790 2.8mm/min kg/cm2(psi) 990(14,080) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 31,800(452) IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.3(0.42) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]

HC 5920

Posted Leave a commentPosted in high flow grades

PROPERTIES Test- Method ASTM Test condition Unit HC- 5920 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 630(8,960) Elongation at break D-638 5mm/min % 3.0 Flexural strength D-790 2.8mm/min kg/cm2(psi) 900(12,800) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 32,500(462) IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.1(0.4) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]