HR 5330T

Posted Leave a commentPosted in heat resistance

PROPERTIES Test- Method ASTM Test condition Unit HR- 5330T Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 780(11,100) Elongation at break D-638 5mm/min % 5.9 Flexural strength D-790 2.8mm/min kg/cm2(psi) 1,200(17,100) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 31,000(449) IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.7(0.5) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]

HR 5330S

Posted Leave a commentPosted in heat resistance

PROPERTIES Test- Method ASTM Test condition Unit HR- 5330S Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 770(10,950) Elongation at break D-638 5mm/min % 5.7 Flexural strength D-790 2.8mm/min kg/cm2(psi) 1,150(16,360) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 31,500 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.4(0.44) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]

HR 5330

Posted Leave a commentPosted in heat resistance

PROPERTIES Test- Method ASTM Test condition Unit HR- 5330 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2(psi) 760(10,810) Elongation at break D-638 5mm/min % 4.7 Flexural strength D-790 2.8mm/min kg/cm2(psi) 1,120(15,930) Flexural modulus D-790 2.8mm/min kg/cm2(103psi) 31,800(452) IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm(ft·lb/in) 2.3(0.42) 1/8″,23°C kg . cm/cm(ft·lb/in) Rockwell hardness D-785 […]