F25 – 03H

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F25-03H Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 13.0 Melting-Point DSC Methode 10°C/min °C 169 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C – 18,6 kgf/ cm2 °C […]

F10 – 03H

Posted Leave a commentPosted in standard types

characteristics Test- Method Units F10-03H Physical properties Density ISO 1183 g/cm3 1.41 Melt flow rate ISO 1133 g/10min 3 Thermal properties Deflection Temperature   1.8MPa ISO 75-1,2 °C 100 Flammability UL94 HB Mechanical properties Tensile Strength  23°C ISO 527-1,2 MPa 69 Norminal strain at break 23°C ISO 527-1,2 % 40 Flexural Strength 23°C ISO 178 […]

F30 – 51

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F30-51 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 27.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F30 – 52

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F30-52 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 28.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F20 – 51

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F20-51 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 10.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F20 -52

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F20-52 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 10.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F40 – 03

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F40 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 52.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F30 – 03

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F30 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 27.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F25 – 03

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F25 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 14.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]

F20 – 03

Posted Leave a commentPosted in standard types

characteristics Test- Method ASTM Conditions Units F20 Physical properties percentage of Filler and Reinforcing Material % – specifc Gravity D792   1.41 Water Absorption D570 23°C 24h % 0.22 Thermal properties Melt-Index D1238   g/10min 9.0 Melting-Point DSC Methode 10°C/min °C 165 Haet Deflection Temperature D648 4,6 kgf/ cm2 °C 158 18,6 kgf/ cm2 °C […]