HR 0370 D

Posted Leave a commentPosted in high heat resistance

PROPERTIES Test- Method ASTM Test condition Unit HR- 0370D Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 480 Elongation at break D-638 5mm/min % 28 Flexural strength D-790 2.8mm/min kg/cm2 720 Flexural modulus D-790 2.8mm/min kg/cm2 24,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 17 1/8″,23°C kg . cm/cm 22 Rockwell hardness […]

HR 0370 F

Posted Leave a commentPosted in high heat resistance

PROPERTIES Test- Method ASTM Test condition Unit HR- 0370F Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 500 Elongation at break D-638 5mm/min % 32 Flexural strength D-790 2.8mm/min kg/cm2 730 Flexural modulus D-790 2.8mm/min kg/cm2 25,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 13 1/8″,23°C kg . cm/cm 17 Rockwell hardness […]

HR 0390

Posted Leave a commentPosted in high heat resistance

PROPERTIES Test- Method ASTM Test condition Unit HR- 0390 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 480 Elongation at break D-638 5mm/min % 25 Flexural strength D-790 2.8mm/min kg/cm2 740 Flexural modulus D-790 2.8mm/min kg/cm2 25,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 15 1/8″,23°C kg . cm/cm 19 Rockwell hardness […]