VE 0856

Posted Leave a commentPosted in flame retardant grades

PROPERTIES Test- Method ASTM Test condition Unit VE- 0856 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 400 Elongation at break D-638 5mm/min % 15 Flexural strength D-790 2.8mm/min kg/cm2 560 Flexural modulus D-790 2.8mm/min kg/cm2 23,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 16 1/8″,23°C kg . cm/cm 22 Rockwell hardness […]

VH 0853

Posted Leave a commentPosted in flame retardant grades

PROPERTIES Test- Method ASTM Test condition Unit VH- 0853 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 400 Elongation at break D-638 5mm/min % 12 Flexural strength D-790 2.8mm/min kg/cm2 590 Flexural modulus D-790 2.8mm/min kg/cm2 24,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 17 1/8″,23°C kg . cm/cm 22 Rockwell hardness […]

VH 0810

Posted Leave a commentPosted in flame retardant grades

PROPERTIES Test- Method ASTM Test condition Unit VH- 0810 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 420 Elongation at break D-638 5mm/min % 10 Flexural strength D-790 2.8mm/min kg/cm2 600 Flexural modulus D-790 2.8mm/min kg/cm2 24,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 19 1/8″,23°C kg . cm/cm 22 Rockwell hardness […]

VH 0800 E

Posted Leave a commentPosted in flame retardant grades

PROPERTIES Test- Method ASTM Test condition Unit VH- 0800E Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 420 Elongation at break D-638 5mm/min % 10 Flexural strength D-790 2.8mm/min kg/cm2 600 Flexural modulus D-790 2.8mm/min kg/cm2 24,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 20 1/8″,23°C kg . cm/cm 22 Rockwell hardness […]