GR 4020

Posted Leave a commentPosted in glass fibre reinforced grades

PROPERTIES Test- Method ASTM Test condition Unit GR- 4020 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 900 Elongation at break D-638 5mm/min % 3.0 Flexural strength D-790 2.8mm/min kg/cm2 1,200 Flexural modulus D-790 2.8mm/min kg/cm2 58,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 1/8″,23°C kg . cm/cm 7 Rockwell hardness D-785 […]

GR 4010

Posted Leave a commentPosted in glass fibre reinforced grades

PROPERTIES Test- Method ASTM Test condition Unit GR- 4010 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 700 Elongation at break D-638 5mm/min % 3.5 Flexural strength D-790 2.8mm/min kg/cm2 1,000 Flexural modulus D-790 2.8mm/min kg/cm2 41,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 1/8″,23°C kg . cm/cm 8 Rockwell hardness D-785 […]

HG 0760 S

Posted Leave a commentPosted in high gloss grade

PROPERTIES Test- Method ASTM Test condition Unit HG- 0760S Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 480 Elongation at break D-638 5mm/min % 20 Flexural strength D-790 2.8mm/min kg/cm2 710 Flexural modulus D-790 2.8mm/min kg/cm2 23,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 16 1/8″,23°C kg . cm/cm 25 Rockwell hardness […]

MP 0660

Posted Leave a commentPosted in metall plating grades

PROPERTIES Test- Method ASTM Test condition Unit MP- 0660 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 430 Elongation at break D-638 5mm/min % 58 Flexural strength D-790 2.8mm/min kg/cm2 650 Flexural modulus D-790 2.8mm/min kg/cm2 23,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 26 1/8″,23°C kg . cm/cm 37 Rockwell hardness […]

MP 0160

Posted Leave a commentPosted in metall plating grades

PROPERTIES Test- Method ASTM Test condition Unit MP- 0160 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 440 Elongation at break D-638 5mm/min % 88 Flexural strength D-790 2.8mm/min kg/cm2 650 Flexural modulus D-790 2.8mm/min kg/cm2 22,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 28 1/8″,23°C kg . cm/cm 37 Rockwell hardness […]

SM 0160 E

Posted Leave a commentPosted in extrusion grade

PROPERTIES Test- Method ASTM Test condition Unit SM- 0160 E Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 370 Elongation at break D-638 5mm/min % 70 Flexural strength D-790 2.8mm/min kg/cm2 510 Flexural modulus D-790 2.8mm/min kg/cm2 15,800 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 34 1/8″,23°C kg . cm/cm 50 Rockwell […]

SM 0150

Posted Leave a commentPosted in extrusion grade

PROPERTIES Test- Method ASTM Test condition Unit SM- 0150 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 450 Elongation at break D-638 5mm/min % 26 Flexural strength D-790 2.8mm/min kg/cm2 660 Flexural modulus D-790 2.8mm/min kg/cm2 22,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 24 1/8″,23°C kg . cm/cm 49 Rockwell hardness […]

SH 0150

Posted Leave a commentPosted in extrusion grade

PROPERTIES Test- Method ASTM Test condition Unit SH- 0150 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 440 Elongation at break D-638 5mm/min % 69 Flexural strength D-790 2.8mm/min kg/cm2 690 Flexural modulus D-790 2.8mm/min kg/cm2 24,000 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 22 1/8″,23°C kg . cm/cm 37 Rockwell hardness […]

AS 0150

Posted Leave a commentPosted in antistatic grade

PROPERTIES Test- Method ASTM Test condition Unit AS- 0150 Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 460 Elongation at break D-638 5mm/min % 12 Flexural strength D-790 2.8mm/min kg/cm2 690 Flexural modulus D-790 2.8mm/min kg/cm2 22,700 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 21 1/8″,23°C kg . cm/cm 33 Rockwell hardness […]

AS 0660 I

Posted Leave a commentPosted in antistatic grade

PROPERTIES Test- Method ASTM Test condition Unit AS- 0660I Mechanical properties Tensile strength at yield D-638 5mm/min kg/cm2 440 Elongation at break D-638 5mm/min % 15 Flexural strength D-790 2.8mm/min kg/cm2 640 Flexural modulus D-790 2.8mm/min kg/cm2 21,200 IZOD notched impact strength D-256 1/4″,23°C kg . cm/cm 21 1/8″,23°C kg . cm/cm 32 Rockwell hardness […]